Abrasive wear behavior of cast iron coatings plasma-sprayed at different mild steel substrate temperatures

作     者：Ya-zhe Xing Qiu-lan Wei Chao-ping Jiang Jian-min Hao 

作者机构：School of Materials Science and Engineering Chang'an University Xi'an 710064 China Department of Automotive Engineering Shaanxi College of Communication Technology Xi'an 710018 China 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2012年第19卷第8期

页      面：733-738页

核心收录：

学科分类：080503[工学-材料加工工程] 0709[理学-地质学] 0819[工学-矿业工程] 0806[工学-冶金工程] 08[工学] 0708[理学-地球物理学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学（可授工学、理学学位）] 0702[理学-物理学] 

基　　金：supported by the Special Fund for Basic Scientific Research of Central Colleges  Chang'an University (No.CHD2009JC131) 

主　　题：cast iron coatings plasma spraying wear bonding 

摘      要：Three kinds of cast iron coatings were prepared by atmospheric plasma spraying. During the spraying, the mild steel substrate temperature was controlled to be averagely 50, 180, and 240℃, respectively. Abrasive wear tests were conducted on the coatings under a dry friction condition. It is ibund that the abrasive wear resistance is enhanced with the substrate temperature increasing. SEM observations show that the wear losses of the coatings during the wear tests mainly result from the spalling of the splats. Furthermore, the improved wear resis- tance of the coatings mainly owes to the formation of oxides and the enhancement in the mechanical properties with the substrate temperature increasing.