Manifestations in Corrosion Prophase of Ultra-high Strength Steel 30CrMnSiNi2 A in Sodium Chloride Solutions

作     者：刘建华 WEN Chen YU Mei LI Songmei WANG Ruiyang 

作者机构：Materials Science & Engineering School Beihang University 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2014年第29卷第2期

页      面：367-373页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0702[理学-物理学] 

基　　金：Funded by the National Natural Science Foundation of China(No.51171011) 

主　　题：30CrMnSiNi2A ultra-high strength steel sodium chloride corrosion prophase 

摘      要：The corrosion behaviors of ultra-high strength steel 30CrMnSiNi2A in sodium chloride solution were studied by weight loss and electrochemical methods. The morphology of corrosion products was observed using scanning electron microscopy（SEM） and the composition was analyzed using an energy dispersive spectroscopy（EDS） and X-Ray diffraction （XRD）. The experimental results showed that the corrosion came from pitting corrosion and the rust layer was composed of outer rust layer γ-FeOOH and inner rust layer Fe_2O_3 with a little β-FeOOH. The correlation between corrosion rate and test time accorded with exponential rule. The corrosion current measured by polarization methods was higher than that calculated by weight loss method after a long-time immersion, the main reason was that,β-FeOOH and γ-Fe_2O_3 transformed by γ-FeOOH led to overestimating corrosion rate. The processes of corrosion prophase were obtained from XRD and EIS results. The corrosion product, Fe（OH）_2 formed at the initial stage stayed at a non-steady state and then consequently transferred to γ-FeOOH, γ-Fe_2O_3 or β-FeOOH.