Rheological and physicomechanical properties of rod milling sand-based cemented paste backfill modified by sulfonated naphthalene formaldehyde condensate
Rheological and physicomechanical properties of rod milling sand-based cemented paste backfill modified by sulfonated naphthalene formaldehyde condensate作者机构:School of Resource and Safety EngineeringCentral South UniversityChangsha 410083China School of Civil EngineeringShaoxing UniversityShaoxing 312000China
出 版 物:《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报(英文版))
年 卷 期:2023年第30卷第2期
页 面:225-235页
核心收录:
学科分类:07[理学] 0806[工学-冶金工程] 0818[工学-地质资源与地质工程] 0903[农学-农业资源与环境] 0802[工学-机械工程] 0703[理学-化学] 0702[理学-物理学]
基 金:financially supported by the National Natural Science Foundation of China(Nos.52104156,52074351,52004330) the Science and Technology Innovation Program of Hunan Province,China(No.2021RC3125) the Natural Science Foundation of Hunan Province,China(No.2022JJ30714)
主 题:rod milling sand sulfonated naphthalene formaldehyde condensate cemented paste backfill rheological properties physicomechanical properties
摘 要:Rod milling sand(RMS)—a coarse sand aggregate—was recycled for cemented paste backfill(CPB)for the underground mined area at the Jinchuan nickel deposit,named rod milling sand-based cemented paste backfill(RCPB).The adverse effects of coarse particles on the transportation of CPB slurry through pipelines to underground stopes resulting in weakening of the stability of the backfill system are well ***,sulfonated naphthalene formaldehyde(SNF)condensate was used for the performance improvement of *** synergistic effect of solid content(SC),lime-to-sand ratio,and SNF dosage on the rheological and physicomechanical properties,including slump,yield stress,bleeding rate,uniaxial compressive strength(UCS),as well as mechanism analysis of RCPB,have been *** results indicate that the effect of SNF on RCPB performance is related to the SNF dosage,lime-to-sand ratio,and *** slump of fresh RCPB with 0.1wt%-0.5wt%SNF increased by 2.6%-26.2%,whereas the yield stress reduced by 4.1%-50.3%,indicating better workability and improved cohesiveness of the *** bleeding rate of fresh RCPB decreased first and then rose with the increase of SNF dosage,and the peak decrease was 67.67%.UCS of RCPB first increased and then decreased with the increase of SNF *** the optimal SNF addition ratio of 0.3wt%,the UCS of RCPB curing for 7,14 and,28 d ages increased by 31.5%,28.4%,and 29.5%,*** beneficial effects of SNF in enhancing the early UCS of RCPB have been ***,the later UCS increases at a slower *** research findings may guide the design and preparation of RCPB with adequate performance for practical applications.