EFFECT OF VACUUM HEAT TREATMENT ON OXIDATION BEHAVIOR OF SPUTTERED NiCrAlY COATING

作     者：M.H. Li X.F. Sun Z.Y. Zhang H.R. Guan W.Y. Hu Z.Q 

作者机构：Institute of Metal Research The Chinese Academy of Sciences Shenyang 110016 China 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：2002年第15卷第1期

页      面：61-66页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

基　　金：The authors thank Prof.H. Y. Lou for sputtering NiCrAlY coating 

主　　题：vacuum heat treatment oxidation sputtered NiCrAlY coating 

摘      要：A bond coat for thermal barrier coating (TBC), NiCrAlY coating, is subjected to vac-uum heat treatment in order to remove internal stress before ceramic top coat is de-posited. The effect of vacuum heat treatment on the oxidation behavior of the sputtered NiCrAlY coating has been investigated. The as-sputtered NiCrAlY coating consists of γ-Ni and b-NiAl phases. After vacuum heat treatment, the sputtered NiCrAlY coating mainly consists of γ -Ni3Al, β-NiAl, γ-Ni, and trace of α-Al2O3 phases. The isothermal oxidation of sputtered NiCrAlY coating with and without vacuum heat treatment has been performed at 1000℃. It is shown that a-Al2O3 formed during vacuum heat treatment acts as nuclei for the formation of a-Al2O3, and the protective a-Al2O3 scale is formed more rapidly on the vacuum heat treated NiCrAlY coating than that formed on the untreated coating. Also the a-Al2O3 scale has a better adherence to the vacuum heat treated NiCrAlY coating. Therefore the vacuum heat treatment improves the oxidation resistance of sputtered NiCrAlY coating.