FATIGUE BEHAVIOR OF CARBURIZED STEEL BEFORE CRACK INITIATION

作     者：Chen, Tiequn Verpoest, I. Deruyttere, A. 

作者机构：Wuhan Inst of Technology Wuhan China 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：1992年第5卷第1期

页      面：58-61页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：carburized steel fatigue microhardness 

摘      要：The fatigue behavior of quenched plus tempered carburized steel before crack initiation has been observed in tension-tension fatigue *** was found that fatigue softening and fatigue hardening coexist in this steel.A transition region near the ease depth of the steel divides the cross section of a round speeimen into two parts:the softened part outwards and the hardened part *** degree of fatigue softening in the case and fatigue hardening in the core is increased with the maximum applied cyclic stress and the number of cycles.