In-situ TEM observation of the evolution of helium bubbles in Mo during He^(+)irradiation and post-irradiation annealing
In-situ TEM observation of the evolution of helium bubbles in Mo during He+ irradiation and post-irradiation annealing作者机构:College of EnergyXiamen UniversityXiamen 361102China Fujian Research Center for Nuclear EngineeringXiamen 361102China Science and Technology on Reactor System Design Technology LaboratoryNuclear Power Institute of ChinaChengdu 610213China
出 版 物:《Chinese Physics B》 (中国物理B(英文版))
年 卷 期:2021年第30卷第8期
页 面:102-112页
核心收录:
学科分类:07[理学] 070203[理学-原子与分子物理] 0805[工学-材料科学与工程(可授工学、理学学位)] 0704[理学-天文学] 0702[理学-物理学]
基 金:Project supported by the National Natural Science Foundation of China(Grant Nos.U1967211 U1832112 and 11975191)
主 题:helium bubbles in-situ TEM observation ion irradiation annealing molybdenum
摘 要:The evolution of helium bubbles in purity Mo was investigated by in-situ transmission electron microscopy(TEM)during 30 keV He^(+)irradiation(at 673 K and 1173 K)and post-irradiation annealing(after 30 keV He^(+)irradiation with the fluence of 5.74×10^(16)He^(+)/cm^(2)at 673 K).Both He^(+)irradiation and subsequently annealing induced the initiation,aggregation,and growth of helium *** had a significant effect on the initiation and evolution of helium *** higher the irradiation temperature was,the larger the bubble size at the same irradiation fluence would *** 1173 K irradiation,helium bubbles nucleated and grew preferentially at grain boundaries and showed super large size,which would induce the formation of *** the same time,the geometry of helium bubbles changed from sphericity to *** polyhedral bubbles preferred to grow in the shape bounded by{100}*** statistical analysis of the characteristic parameters of helium bubbles,the functions between the average size,number density of helium bubbles,swelling rate and irradiation damage were ***,an empirical formula for calculating the size of helium bubbles during the annealing was also provided.