Effect of manufacturing methods of AgCl/Al_2O_3 catalyst on selective catalytic reduction of NO_x

作     者：Satoshi Kishida Dong-Ying Ju Hirofumi Aritani 

作者机构：Advanced Science Research Laboratory Saitama Institute of Technology 1690 Fusaiji Fukaya 369-0293 Japan Faculty of Engineering Saitama Institute of Technology 1690 Fusaiji Fukaya 369-0293 Japan Department of Life Science & Green Chemistry Saitama Institute of Technology 1690 Fusaiji Fukaya 369-0293 Japan 

出 版 物：《Journal of Environmental Sciences》 (环境科学学报（英文版）)

年 卷 期：2011年第23卷第6期

页      面：1033-1037页

核心收录：

学科分类：081705[工学-工业催化] 08[工学] 0817[工学-化学工程与技术] 

基　　金：supported by the Open Research Center of Saitama Institute of Technology 

主　　题：AgCl/Al2O3 catalytic reduction SCR NOx 

摘      要：The AgCl/Al2O3 catalyst has potential for use in the selective catalytic reduction（SCR） of NOx.A compound hydrocarbon,following oxygenation is used as a type of reducing *** this experiment,the AgCl/Al2O3 catalyst was produced by four different methods,and the differences among their reduction catalysis of NOx were *** was used as a type of reducing agent.X-ray diffraction analysis was performed to study the crystalline structure and scanning electron microscope and transmission electron microscope（TEM） were applied to determine the *** results indicated that,in the range of 350-400℃,there was no significant difference on the NOx reduction rate;however,there was dispersion at high and low temperature *** size of the AgCl particles was about 20-100 nm.