Effect of oxygen plasma treatment on the nanofiltration performance of reduced graphene oxide/cellulose nanofiber composite membranes
Effect of oxygen plasma treatment on the nanofiltration performance of reduced graphene oxide/cellulose nanofiber composite membranes作者机构:Department of Chemical EngineeringMonash UniversityVIC3800Australia College of the Environment&EcologyXiamen UniversityXiamenFujian361005China
出 版 物:《Green Chemical Engineering》 (绿色化学工程(英文))
年 卷 期:2021年第2卷第1期
页 面:122-131页
核心收录:
学科分类:080706[工学-化工过程机械] 08[工学] 0807[工学-动力工程及工程热物理] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学] 0822[工学-轻工技术与工程] 0702[理学-物理学]
基 金:the Australian Research Council(Project No.IH170100009)
主 题:Graphene oxide Membrane Nanofiltration Cellulose nanofibers Oxygen plasma treatment
摘 要:Graphene based nanosheets have been widely used as building blocks for fabrication of superior separation membrane for water *** particular,membranes made of reduced graphene oxide(rGO)show better stability compared with graphene oxide(GO).However,densely stacked of rGO often results in low water *** this study,cellulose nanofibers(CNFs)were incorporated into the rGO laminates by vacuum filtration of dilute GO/CNF solution and thermal reduction at 150C for 1.5 *** resulting rGO/CNF membrane was treated with oxygen plasma for 1–4 min to create nanopores on the membrane surface for the purpose of enhancing nano-filtration *** results showed that the optimum membrane performance was obtained by using the equal amount of GO(31.83 mg m^(-2))and CNFs accompanied by 3 min of plasma treatment,exhibiting a pure water permeance of 37.23.9 L m^(-2)h^(-1)bar^(-1)maintaining a rejection above 90%for Acid Fuchsin(1.2×1.1 nm),Rose Bengal(1.5×1.2 nm)and Brilliant Blue(2.2×1.7 nm).