Relationship between interfacial structure and property of steel-mushy Al-28Pb bonding pate
Relationship between interfacial structure and property of steel-mushy Al-28Pb bonding pate作者机构:Department of Mechanical Engineering Beijing Jiaotong University Beijing 100044 China Department of Mechanical Engineering Tsinghua University Beijing 100084 China Anshan Automobile Fittings Factory Anshan 114014 China
出 版 物:《Journal of Central South University of Technology》 (中南工业大学学报(英文版))
年 卷 期:2006年第13卷第1期
页 面:12-16页
核心收录:
学科分类:080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0802[工学-机械工程] 080201[工学-机械制造及其自动化]
基 金:Projects(50274047 50304001)supportedbytheNationalNaturalScienceFoundationofChina project(105040)supportedbytheMinistryofEducationofPRCFoundation projectsupportedbytheNaturalScienceFoundationofBeijing projectsupportedbyBeijingJiaotongUniversityFoundation
主 题:interfacial structure ratio of Fe-Al compound interfacial shear strength
摘 要:The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The results show that there is a nonlinear relationship between the ratio of Fe-Al compound at the interface and the interfacial shear strength. When the ratio of Fe-Al compound at the interface is smaller than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength increases gradually; when the ratio of Fe-Al compound at the interface is larger than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength decreases continuously; when the ratio of Fe-Al compound at the interface is 71.4%, the largest interfacial shear strength 70.2MPa is obtained.