Effect of Application Rates of Assistant Agents on Properties of Nano SiO_2/NR Composites

作     者：赵同建 符新 

作者机构：Rubber Research Institute Chinese Academy of Tropical Agricultural Sciences Chinese Agricultrural Ministry Key Laboratory of Natrural Rubber Processing School of Chemical Engineering and Materials Hainan University 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2009年第24卷第3期

页      面：387-392页

核心收录：

学科分类：07[理学] 070205[理学-凝聚态物理] 08[工学] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0702[理学-物理学] 

基　　金：Funded by the Special Fund of Basic Scientific Research of Rubber Research Institute of CATAS Key Laboratory of Ministry of Agriculture for Natural Rubber Processing (No. xjszx-13 and No. xjsbywfzx2009-19, 706057) 

主　　题：assistant agents nano-SiO2 NR composites 

摘      要：Nano SiO2/NR composites were prepared through blending nano SiO2 emulsion with natural rubber latex and then concreting with acetic acid. The emulsion nano SiO2 was prepared with Na2SiO3-9H2O and hydrochloric acid under the reaction of the assistant agents. The was analyzed effect of the application rates of assistant agents such as silane coupling agent, surfactant, nucleating agent and dispersant on the properties and interface structure of the nano SiO2/NR composites with IR, TEM, SEM, DMA was analyzed. An orthogonal test was arranged to select optimum condition. The results show that the best combination for preparing nano SiO2/NR composites is as follows： the rate of the silane coupling agent （TESPT）, the surfactant（dodecyl benzene sulfonate natrium）, nucleating agent（AlCl3） and dispersant（ethylene diamine tetraacetie acid） in the course of preparing nano SiO2 are 15%, 2.0%, 2.5% and 0.4%, respectively. Several replications in the experiment had produced desirable nano SiO2 products and nano SiO2/NR composites with better properties.